ESR spectroscopic analyses of the deep-green solutions of living poly(2-isopropenylnaphthalene) [poly(2-IPN)] in THF at −80°C provided no evidence of the presence of radical anions as long as butyllithium (BuLi) was used as initiator. In contrast to this finding, radicals could indeed be detected if the polymerization was performed with metallic potassium in THF. These radicals were found to be only stable at low temperatures. UV/VIS spectra of solutions of 2-IPN in THF or toluene and of catalytic quantities of BuLi were recorded at temperatures between −45 and +20°C. On heating to >0°C, the colour of the deep-green solution changes irreversibly to reddish-brown, and this colour change is a…

Blockcopolymere aus 2-Isopropenylnaphthalin und Hexamethylcyclotrisiloxan, 7

Anionic polymerization of 2-isopropenylnaphthalene (2-IPN), with butyllithium in THF at −78°C was terminated with ethylene oxide and the resulting terminal alkoxide was used to initiate the polymerization of hexamethylcyclotrisiloxane (D3) at +40°C. This led to the formation of AB-block copolymers which were coupled to ABBA-block copolymers by addition of dichlorodimethylsilane. ABBA-blockcopolymers were obtained with contents of polymethylsiloxane (poly(DMS)) between 77 and 84% of weight and block molecular weights between 1 700 and 27 000 (poly(2-IPN)) and 13 000 and 240 000 (poly(DMS)). Phase separation in polymer films casted from different solvents was studied by electron microscopy an…