A procedure is described for the preparation of a block copolymer with A-B-A sequences in which ω-ω′-dihydroxy-poly-(ethylene glycol) is inserted between two polymeric monoacidic chains of polycaproamide and bonded to them by means of ester links. The resulting material was characterized. The copolymer is isomorphous with the polycaproamide. Thermal treatments induce a crystalline transition γ α as in polycaproamide. The influence of the moisture content on the glass transition temperature and on the storage modulus is discussed. Ein Verfahren zur Herstellung eines Blockcopolymers mit A-B-A-Sequenzen wird beschrieben. In dem Copolymer ist ω-ω′-Dihydroxy-polyethylenglycol uber Esterbindungen…

Preparation and mechanical characterization of fibres from a new copoly(ether-ester-amide) are reported. The mechanical characteristics are slightly lower than those of polyamide 6, but satisfactory for textile use, and the fibres have larger moisture absorption. This gives rise to more comfortable fibres preventing the accumulation of electrostatic charges. Die Herstellung und mechanische Charakterisierung von Fasern aus einem neuen Copoly(ether-ester-amid) werden beschrieben. Die mechanischen Eigenschaften sind etwas schlechter als die von Polyamid 6, aber ausreichend fur textile Anwendungen. Die Fasern weisen eine grosere Feuchtigkeitsabsorption auf. Dies fuhrt zu einem angenehmeren Verh…