Strain induced renormalization of transport properties in UPt3 thin films

The growth of sputter deposited UPt3 thin films on Al2O3 (1012), LaAlO3 (111) and SrTiO3 (111) was investigated. We found strongly 0001-textured growth of UPt3 in a small compositional range of 23–25% uranium content. For Al2O3-and LaAlO3-substrates no in-plane order could be observed whereas epitaxial growth was initiated on SrTiO3 (111): The growth can be identified as Vollmer-Weber like resulting in the formation of large lateral strain as a consequence of the growth mode and a lattice misfit of −4.3% between UPt3 (0001) and SrTiO3 (111). Strong deviations from the typical heavy-fermion characteristics in electronic transport properties like resistivity, magnetoresitivity and Hall-effect…