Influence of the mode of introduction of a reactive element on the high temperature oxidation behavior of an alumina-forming alloy. Part I: Isothermal oxidation tests

Several routes of yttrium introduction were applied to test the high temperature oxidation performance of a FeCrAl alloy. Isothermal oxidation tests were described in a previous paper (Part I of this paper in this journal, 2004, 55, 352). Cyclic oxidation tests were performed in air under atmospheric pressure on blank specimens, Y 2 O 3 sol-gel coated-, Y 2 O 3 metal-organic chemical vapor deposited (MOCVD)-, yttrium ion implanted-alloys, as well as on a steel containing 0.1 wt.% of yttrium as an alloying element. For the 20 hours cycles, all the samples, except FeCrAl-0.1Y, exhibit weight losses after a few cycles, indicating drastic spallation of the oxide scales. The MOCVD coated specime…