DIELECTRIC PROPERTIES OF LEAD-FREE [(1-x)(Na0.5Bi0.5)-xBa]Zr1−yTiyO3CERAMICS (x = 0.01, 0.06, 0.085, 0.09, 0.1 AND y = 0.96, 0.97)
ABSTRACT Lead-free ceramics based on (Na0.5Bi0.5TiO3, NBT)-(Ba(Ti, Zr)O3, BTZ) were prepared by solid phase synthesis and hot pressing sintering process and their dielectric properties have been studied. The obtained results were compared with these for pure NBT. The obtained samples show pure perovskite structure. Low frequency (100 Hz-100 kHz) investigations reveal the diffuse phase transitions and relaxorlike behaviour. The obtained results are discussed in terms of inhomogeneity of ions distribution, their ferro- and antiferroactivity and internal stresses. The NBT-BTZ system is expected to be a new promising candidate for lead-free electronic ceramics.
Electrical Transport in Lead-Free [(1−x)(Na0.5Bi0.5)-xBa]Zr1 - yTiyO3Ceramics (x = 0, 0.06, and y = 0, 0.96)
Lead-free ceramics based on (Na 0.5 Bi 0.5 TiO 3 , NBT)-(Ba(Ti,Zr)O 3 , BTZ) were prepared by solid phase hot pressing sintering process and their ac (σ ac ) and dc (σ dc ) conductivity have been studied (303–753 K). Low frequency (100 Hz–100 kHz) ac conductivity obeys power law σ ac ∼ ω s characteristic for disordered materials. The frequency exponent s is a decreasing function of temperature and tends to zero at high temperatures. Dc conductivity has thermally activated character and possesses four linear parts with four different activation energies and some discontinous changes. However, σ ac (T) possesses two linear parts with two different activation energies and more discontinuous ch…