Effect of dentin surface pretreatment with four conditioning agents on micro-shear bond strength of a self-adhesive cement.

To evaluate the effect of dentin surface pretreatment with four conditioning agents on the micro-shear strength of a self-adhesive cement.32 specimens of 6 mm high x 4 mm wide with dentin exposure were obtained and divided into four groups of NaOCI, CHX, EDTA and AgNPs (n = 8). 2 mL of each treatment agent was applied to the dentin for 60 seconds. Composite resin cylinders measuring 3 mm x 2 mm were cemented with RelyX U200 self-adhesive cement. Micro-shear testing was performed after 24 hours and one week (n = 4) with a 1 mm/min; failure values were recorded in MPa. The failure pattern was evaluated with a stereomicroscope at 20x. The Kruskal-Wallis test was used to evaluate differences be…