Photocatalytic activity of anatase-nickel ferrite heterostructures
The simple co-precipitation route was used to couple commercial TiO2 anatase nanopowder with nickel ferrite (NiFe2O4). The morphology and the crystalline structure of composite nanoparticles were characterised by TEM, N2 adsorption-desorption, XRD and Rietveld refinement, XPS and XAS. The optical and magnetic properties were investigated. After co-precipitation NiFe2O4 nanoparticles, composed of spinel ferrite crystal phase, were formed on the surface of TiO2 anatase nanopowder. The TiO2/NiFe2O4 composite oxide demonstrated large specific surface area, high visible light absorption efficiency and efficient charge carrier separation, compared to pristine anatase TiO2 or pristine NiFe2O4, rep…
Facile synthesis of magnetically separable CoFe2O4/Ag2O/Ag2CO3 nanoheterostructures with high photocatalytic performance under visible light and enhanced stability against photodegradation
Riga Technical University supported the preparation of this manuscript from the Scientific Research Project Competition for Young Researchers No. ZP-2016/7. The authors wish to kindly acknowledge the financial support of HZB, Estonian Research Council (PUT1096, PUT735 and IUT2-25) and Estonian Centre of Excellence in Research Project “Advanced materials and high-technology devices for sustain-able energetics, sensorics and nanoelectronics” TK141 (2014–2020.4.01.15-0011).
Ag sensitized TiO2 and NiFe2O4 three-component nanoheterostructures: synthesis, electronic structure and strongly enhanced visible light photocatalytic activity
This study reports on the synthesis and characterisation of two- and three-component visible light active photocatalytic nanoparticle heterostructures, based on TiO2 and NiFe2O4 and sensitized with Ag. We observe that a Ag content as small as 1 at% in the TiO2/NiFe2O4 heterostructure increases by more than an order of magnitude the rate constant for the visible light photocatalytic process. We rationalise this in terms of the measured structure and electronic structure data of the binary and ternary combinations of the component materials and focus on details, which show that an optimised deposition sequence is vital for attaining high values of photocatalytic efficiency, because the charge…
Solvothermal synthesis derived Co-Ga codoped ZnO diluted magnetic degenerated semiconductor nanocrystals
Authors kindly acknowledge to the Estonian Research Council ( PUT1096 , IUT2-25 , PUT735 ), the Estonian Centre of Excellence in Research project “Advanced materials and high-technology devices for sustainable energetics, sensorics and nanoelectronics (TK141), and the financial support of HZB. We are grateful to the staff of BESSY II for the assistance and co-operation during the synchrotron-based measurements.
Reversible Photodoping of TiO2 Nanoparticles for Photochromic Applications
Financial support from the Estonian Research Council (IUT2-25, IUT2-26, and PUTJD680) is gratefully acknowledged. This work was supported by the Academy of Finland (decision numbers 141481 and 286713) and by the EU through the European Regional Development Fund (Center of Excellence for Zero Energy and Resource Efficient Smart Buildings and Districts-ZEBE, 2014-2020.4.01.15-0016). Work is supported by the Latvian Academy of Sciences in the framework of FLPP (Plasmonic oxide quantum dots for energy saving smart windows, lzp-2018/1-0187).