Analysis of plasticization and reprocessing effects on the segmental cooperativity of polylactide by dielectric thermal spectroscopy
Abstract In the present study, the dielectric properties of both neat and plasticized polylactide submitted to repeated extrusion and injection processes to simulate recycling were analysed. The dielectric relaxation spectrum, consisting of β and α relaxation, revealed the relevance of both acryl-PEG based plasticization and thermo-mechanical degradation induced by repeated extrusion and grinding-injection reprocessing cycles on polylactide (PLA). The β-relaxation has its origin in the intramolecular local motions of pendant groups of the PLA backbone, while the α-relaxation is representative of the intermolecular large-scale segmental motions of the PLA backbone. The addition of acryl-PEG …
Recovery of dissolved methane through a flat sheet module with PDMS, PP, and PVDF membranes
Abstract A degassing contactor using a flat sheet membrane module (FM) was operated in sweep gas mode to study the performance of several commercial polymer membranes, both dense (polydimethylsiloxane, PDMS) and microporous (polypropylene, PP, and polyvinylidenefluoride, PVDF), for the recovery of dissolved methane from water. Non-steady state experiments were conducted at different liquid (QL, 3.5–40.5 L h-1) and gas flow rates (QN2, 0.05–15.00 L h-1). In the case of PDMS, PP, and when PVDF was operated at moderate high QL (≥ 21 L h-1), similar methane removal efficiencies (RE) were obtained. In the case of PVDF operated at relatively low QL (3.5 L h-1), a lower RE was observed. A model fo…