Macroscopic persistent currents in laser deposited YBa2Cu3O7 films
We have investigated persistent currents in a superconducting YBa2Cu3O7 ring of about 1 cm diameter, which was deposited as c-axis textured film on a SrTiO3 substrate by laser ablation. The currents were registered, via their magnetic field distribution, with a small vibrating pick-up coil. At 77 K persistent currents with negligible decay over 103 s have been observed below a critical current density jc=0.9×105 A/cm2, both for a field-cooled and a zero-field-cooled sample. This demonstrates that it is possible to fabricate dissipationless devices of such films on a relatively large scale.
Investigation of the epitaxy of thin YBa2Cu3O7-delta films
Abstract The degree of epitaxy of thin sputtered and laser ablated films have been investigated by Raman spectroscopy. Using the selection rules for Raman scattering for the different phonons in YBa 2 Cu 3 O 7−δ the superconducting films on SrTiO 3 and MgO are found to be epitaxially grown with the c -axis perpendicular to the substrate. On ZrO 2 the films also grow with their c -axis perpendicular to the substrate, but with randomly oriented a / b -directions in the plane of the film.