2009
Abstract The interaction between Ni/SiO 2 (18 wt%) and thiophene was studied by thermal gravimetric analysis (TGA) and in a fixed-bed reactor. The samples were prepared by incipient wetness impregnation and reaction was realized in hydrogen flow at 280–360 °C in the presence of 10–40 mbar of thiophene. It is found that sulfidation of Ni is not complete in TGA experiments and the maximum achievable transformation degree depends not only on the temperature and thiophene pressure, but also on the sample weight and the gas flow rate. The maximum transformation degree is shown to vary reversibly when conditions are changed. Analysis of the reaction products during sulfidation in a fixed-bed reac…
Kinetics of thiophene reactive adsorption on Ni/SiO2 and Ni/ZnO.
2008
Abstract Kinetics of thiophene reactive adsorption on Ni/SiO2 and Ni/ZnO was studied by thermal gravimetric analysis at 280–360 °C under 5–40 mbar of thiophene in H2. In the case of Ni/SiO2 the interaction proceeds in two steps: a rapid surface reaction is followed by a slower bulk transformation into Ni3S2. Maximum Ni conversion depends on reaction conditions and observed conversion profiles can be described by an exponential equation corresponding to a reaction of first order relatively to both sulfidable Ni amount and thiophene. The interaction between Ni/ZnO and thiophene proceeds in a rather different manner. A rapid increase of weight, similar to the first stage observed on Ni/SiO2, i…