Effect of microstructure and chemical composition on localized corrosion resistance of a AISI 304L stainless steel after nanopulsed-laser surface melting
Abstract Changes induced in the surface properties of AISI 304L stainless steel when it is treated with a nanopulsed ytterbium-doped fiber laser were investigated to determine the microscale distribution of its physico-chemical properties. A Gaussian energy distribution was created with a radius of 71 μm (1/e2) at the focal point. Local investigations were carried out using transmission electron microscopy to consider the effect of overlapping individual laser impacts. The results obtained reveal that laser surface melting leads to changes in the crystallographic structure of the steel through the formation of a δ-ferritic phase. It also results in the creation of an oxide layer that increa…
Nanosecond laser surface modification of AISI 304L stainless steel: Influence the beam overlap on pitting corrosion resistance
Abstract Surface modifications of AISI 304L stainless steel by laser surface melting (LSM) were investigated using a nanosecond pulsed laser-fibre doped by ytterbium at different overlaps. The objective was to study the change in the corrosion properties induced by the treatment of the outer-surface of the stainless steel without modification of the bulk material. Different analytical techniques such as scanning electron microscopy (SEM), X-ray diffraction (XRD), and glow discharge optical emission spectrometry (GDOES) were used to characterize the laser-melted surface. The corrosion resistance was evaluated in a chloride solution at room temperature by electrochemical tests. The results sh…