Holographic recording of surface relief gratings in tolyle-based azobenzene oligomers
Abstract Holographic recording of surface relief gratings (SRG) in tolyle-based azobenzene oligomer films have been carried out at 514.5 nm. It was experimentally studied by spectroscopic and AFM methods. The maximum surface modulation amplitude was 35 nm. SRG formation is explained by the mean-field model and by the photodegradation of chromophores enabling the directional mass transport as the result of trans–cis transformations. The conclusion is made that SRG are stable but the diffraction efficiency (DE) changes are due to the complementary decaying amplitude-phase gratings. Strong polarization dependences of transmitted and reflected DE are found. They are explained by the diffraction…
Holographic properties of azobenzene oligomers with differently bonded chromophore groups
Holographic properties of two types (I and II, specified in the text) of azobenzene oligomers (ABO) have been experimentally studied in the spectral region of low absorption at 633 nm. In the case of type I ABO the chromophore groups were covalently bonded to either tolyl-polyurethane or hexamethylene-polyurethane matrix. In the case of type II ABO azobenzene chromophores were dispersed in polystyrene matrix, and their concentration was varied from 0.005 to 0.200 mol/l. Samples were in the form of 10 µm thick films. In both cases the diffraction efficiency exposure time dependences were measured for the holographic grating period of 2 (m at 633 nm. The diffraction efficiency of more than 2%…