Modified arabinoxylan-based films. Part B. Grafting of omega-3 fatty acids by oxygen plasma and electron beam irradiation.
Arabinoxylans (AXs) are byproducts of the cereal milling industry. To obtain high-value products, AXs have been used as a film-forming agent. Hence, AX-based films are poor water vapor barriers. The objectives of this study were to graft omega-3 (omega3) fatty acids onto AX polymeric chains by using two new technologies: cold plasma and electron beam (EB) irradiation. Results show that the surface hydrophobicity of the modified films is higher than that of a waxy coating or a low-density polyethylene (LDPE) film. In addition, FTIR spectroscopy analysis reveals vibration bands attributed to new chemical functions. Finally, a decrease in water vapor permeability (WVP) is obtained for the film…
Modified arabinoxylan-based films
Abstract Oxygen plasma and electron beam irradiation were used to graft hydrophobic substances and by this way, to reduce water vapor permeability (WVP) of arabinoxylan-based (AX-based) films. Stearyl acrylate (SA) and stearyl methacrylate (SM) were used as reactive monomers. The homogeneous AX-based films, which were pre-activated by oxygen plasma and impregnated with a solution of SA before being exposed to an electron beam (EB), had contact angles that increased from 71° (untreated films) to 122° (treated films). A decrease of about 24% in the WVP was obtained and new chemical groupings were observed on the FTIR spectra of these films. Acrylate monomers were also dispersed into the arabi…