0000000000680918
AUTHOR
Ernő Kuzmann
Icems and dcems study of Fe layers evaporated onto Al and Si
Thin layers of57Fe (2.5 nm, 10 nm and 70 nm thickness), vacuum evaporated onto Al and Si plates, have been investigated by conversion electron Mossbauer spectroscopy (CEMS). The measurements were performed employing both a proportional counter and a channeltron for conventional and ultrahigh-vacuum integral CEMS (UHV-ICEMS) studies, respectively, and a channeltron for depth-selective CEMS (DCEMS). The phase analysis of the layers on base of experimental results has indicated the presence of metallic iron and one or two iron compounds, ascribed to iron reaction products formed with the residual gas during evaporation. These products are most likely rather stable iron nitrides, are more or le…
Influence of sulphite on the passivation of iron
Abstract Mossbauer spectroscopy and electrochemical measurements were used to study the passivation of iron and steels in a sulphite containing solution. The potentiodynamic curves show that passivation occurs at −140 mV potential vs saturated calomel electrode ( sce ). The main phase of the passive layer was found to be γ-FeOOH, while FeSO 4 ·H 2 O on the surface and FeSO 3 ·3H 2 O inside the layer were identified as minor phases in the case of polarization in a solution of pH 3.37. Only γ-FeOOH was observed on the surface of samples polarized at pH 6.6.