Impact of Si on the high-temperature oxidation of AlCr(Si)N coatings

The resistance of wear protective coatings against oxidation is crucial for their use at high temperatures. Here, three nanocomposite AlCr(Si)N coatings with a fixed Al/Cr atomic ratio of 70/30 and a varying Si-content of 0 at.%, 2.5 at.% and 5 at.% were analyzed by differential scanning calorimetry, thermogravimetric analysis and X-ray in order to understand the oxidation behavior depending on their Si-content. Additionally, a partially oxidized AlCrSiN coating with 5 at.% Si on a sapphire substrate was studied across the coating thickness by depth-resolved cross-sectional X-ray nanodiffraction and scanning trans-mission electron microscopy to investigate the elemental composition, morphol…