Désirée Weller
Cylindrical Polymer Brushes with Elastin-Like Polypeptide Side Chains
Monodisperse high molar mass elastin-like polypeptide macromonomers comprising 20 pentasequences (M = 8332 g/mol) were radically polymerized to high degrees of polymerization Pw = 590. Polymerization was conducted in water well above the lower phase transition temperature, i.e., in the phase separated regime. The resulting polymers adopt a cylindrical shape as demonstrated by AFM pictures of solutions spin-cast on mica. The directional persistence of the cylindrical brushes was determined by static light scattering to Kuhn statistical segments lengths lk = 120 nm at 5 mM aqueous NaCl solution which decreased to lk = 54 nm at 0.65 M NaCl. Upon polymerization the phase transition temperature …
Solution Properties and Potential Biological Applications of Zwitterionic Poly(ε-N-methacryloyl-l-lysine)
Poly(e-N-methacryloyl-l-lysine) (PMALys) was synthesized by free radical polymerization yielding a zwitterionic polymer with Mw = 721 000 g mol–1. The polymer dissolves in pure water as well as in aqueous salt solution up to 5 M NaClO4 and over wide range of pH values (1.3 ≤ pH ≤ 12.7) as single chains without any sign for aggregate formation. The zwitterionic polymer shows an expanded random coil structure at and close to isoelectric conditions and further expands upon addition of acid and base, respectively. The polymer fulfills four major prerequisites for a promising nano carrier in potential biomedical applications: (1) It is biocompatible, indicated by a low cytotoxicity. (2) It does …