Efficacy of preheated chelating agents on calcium ion removal from instrumented root canals
Background The heating of chelating agents such as EDTA increases dentin wettability by decreasing surface tension. However, the calcium ion release effect of preheated chelating agents in instrumented root canals has not yet been mentioned. In this study, it was aimed to evaluate the number of calcium ions removed by the pre-heated chelating agents from the root canals. Material and Methods After 51 bovine teeth were instrumented, three of them were separated as negative controls and the remaining teeth were divided into six groups according to the temperature of the solution (at 22 or 37ºC): EDTA-22, CITRIC-22, QMix-22, EDTA-37, CITRIC-37 and QMix-37. Following irrigation, calcium ion lev…
Investigation of water sorption and aluminum releases from high viscosity and resin modified glass ionomer.
Background High viscosity glass ionomer cement (HVGIC) and resin-modified glass ionomer cement (RMGIC) have recently been clinically preferred thanks to their numerous advantages. However, initial moisture contamination has a negative effect on the mechanical and physical properties of these cements. The aim of this study was in vitro of HVGICs and RMGICs, with and without surface protection, on water sorption, solubility and release of aluminum. Material and Methods In this study, as HVGICs; Equia Forte, IonoStar Plus, Riva Self Cure; as RMCIS, Ionolux and Riva Light Cure; and as control, Z250 universal composite was used. Equia coat, Voco varnish and Riva coat were chosen as surface prote…