Conductivities and silver electrode polarization resistance of solid electrolyte ceramics from ZrO 2 -Y 2 O 3 powder synthesized in air plasma

Ceramic specimens have been obtained from the powder of ZrO2-7.5 mol% Y2O3 having a specific surface area of 30 m2/g synthesized in air plasma. The novelty of this research lies in the fact that the plasma process makes it possible to prepare so-called nanopowders with a particle size less than 100 nm, possessing specific physical, chemical and technological properties. The sintered density of the specimens was 94–96% of the theoretical value, 6.001 g/cm3. The X-ray diffraction pattern of the specimens corresponded to a face-centered cubic lattice. Impedance in the frequency range of 100 Hz–15 MHz and d.c. polarization curves in a potential range of −10 to 10 mV were measured in the tempera…