Influence of applied strain on the microstructural corrosion of AlMg2 as-cast aluminium alloy in sodium chloride solution
International audience; The corrosion behavior of ISO AlMg2 (AA5052) was studied at the microscale using the Electrochemical Microcell Technique. The influence of plastic deformation on the corrosion resistance of this alloy was also examined. After polishing, pitting at small copper-enriched precipitates and structural etching were observed. After deformation, numerous slip bands were found in grains. After 5.5% plastic strain, the global electrochemical behavior of samples was significantly affected. Pitting potential was decreased in sites containing slip bands or in sites with large strain gradients (measured using microgauges deposited by lithography).
Influence of Plastic Deformation on the Corrosion Behaviour of As-Cast AlMg2 and AlCu4Mg1 Aluminium Alloys in NaCl Solution
The influence of plastic deformation on the corrosion behavior of as-cast AlMg2 and AlCu4Mg1 aluminum alloys was studied at the microscale using the Electrochemical Microcell Technique and surface microgauges. It was shown that large strain gradients develop locally. The corrosion behavior of both alloys was affected by plastic deformation. The most active sites contain large strain gradients in AlMg2 and cracks with damage in the matrix in AlCu4Mg1.