The use of the indentation test for studying the solidification behaviour of different semicrystalline polymers during injection moulding
Summary: An in-line method for monitoring the solid-ificationprocess during injection molding of semicrystallinepolymers (demonstrated previously in J. Appl. Polym. Sci.2003, 89, 3713) is based on a simple device, where anadditional ejector pin is pushed on the injection molded partatdifferenttimesduringthesolidificationphase.The‘inden-tation depth profile’, i.e., residual deformation as a functionoftime,wasobtainedandallowedtodeterminetheevolutionof the solidification front in the mold as a function of thecooling time. The present work shows the reliability andthe powerfulness of the aforementioned method for a largevariety of different semicrystalline polymers (PET, PBT,polyamide-6 PA6, isota…
Indentation test as a tool for monitoring the solidification process during injection molding
An inline method for monitoring the solidification process during the injection molding of semicrystalline polymers is demonstrated. The method has been applied to various poly(ethylene terephthalate) (PET) and poly(buthylene terephthalate) (PBT) samples. The technique is based on a simple device by which an additional ejector pin is pushed onto the injection-molded part with a fixed force at different times during the solidification phase while the mold remains closed. The residual deformation (the so-called indentation depth) due to the applied load is measured offline after ejection. By the performance of indentation at different times during the cooling phase, an indentation depth profi…