Study of the Growth Mechanism of some Oxide Scales on Alloy 230 in High Temperature Vapor Electrolysis (HTVE) Conditions

Alloy 230 (also named Haynes® 230) was tested as interconnect for production of hydrogen via High Temperature Vapor Electrolysis (HTVE). Samples were oxidized at 800°C in the both atmospheres representative of the HTVE operating conditions: Ar-1%H2-9%H2O (for cathode side) and air (for anode side). The high temperature oxidation behaviour was studied in both atmospheres together with the electrical conductivity of the thermally grown oxide scales. Oxidation kinetics indicated lower oxidation rate in H2/H2O compared to air (kp = 3.8 .10-15 g2.cm-4.s-1 in H2/H2O and kp = 1.6 .10-14 g2.cm-4.s-1 in air). The corrosion products were characterized by scanning electron microscopy associated with X…