Iron-containing phases in metallurgical and coke dusts as well as in bog iron ore

Abstract Several samples of dusts from steel and coke plants (collected mostly with electro filters) were subjected to the investigation of content of mineral phases in their particles. Additionally, sample of bog iron ore and metallurgical slurry was studied. Next, the magnetic susceptibility of all the samples was determined, and investigations of iron-containing phases were performed using transmission Mössbauer spectrometry. The values of mass-specific magnetic susceptibility χ varied in a wide range: from 59 to above 7000 × 10−8 m-3·kg−1. The low values are determined for bog iron ore, metallurgical slurry, and coke dusts. The extremely high χ was obtained for metallurgical dusts. The …