From Spherical Mesopores to Worm-Shaped Mesopores : Morphology Transition in Titania–Polystyrene-b-poly(ethylene oxide) Composite Films with Increasing Sol–Gel Reaction Time
A morphology transition from spherical mesopores to worm-shaped mesopores within titania block copolymer composite thin films has been observed by varying the sol–gel reaction time from 40 min to 48 h in the four-component templating system of polystyrene-$\mathit{b}$-poly(ethylene oxide) (PS-$\mathit{b}$-PEO), 1,4-dioxane, concentrated HCl, and titanium tetraisopropoxide (TTIP) with a PS-$\mathit{b}$-PEO mass concentration of 0.25 wt.-%. The impact of the sol–gel reaction time on the local structure, long-range lateral structure, and vertical structure of the as-prepared, calcined, and UV-degraded thin films as well as the structural changes in solution have been systematically investigate…
Hierarchically Structured Titania Films Prepared by Polymer/Colloidal Templating
Hierarchically structured titania films for application in hybrid solar cells are prepared by combining microsphere templating and sol-gel chemistry with an amphiphilic diblock copolymer as a structure-directing agent. The films have a functional structure on three size scales: (1) on the micrometer scale a holelike structure for reduction of light reflection, (2) on an intermediate scale macropores for surface roughening and improved infiltration of a hole transport material, and (3) on a nanometer scale a mesoporous structure for charge generation. Poly(dimethyl siloxane)-block-methyl methacrylate poly(ethylene oxide) (PDMS-b-MA(PEO)) is used as a structure-directing agent for the prepara…
Morphology evolution in mesoporous titania block copolymer composite films with increasing Sol-Gel reaction time
A morphology evolution of thin films of titania from spherical mesopores to worm-shaped mesopores was realized by simply varying the sol–gel reaction time from 46 min to 25 h in the quadruple system consisting of polystyrene–block-poly(ethylene oxide) (PS–b-PEO), 1,4-dioxane, concentrated HCl, and titanium tetraisopropoxide (TTIP). Imaging techniques including scanning electron microscopy (SEM) and atomic force microscopy (AFM) were applied to investigate the local structure change of the as-prepared, calcined, and UV-degraded composite films. Grazing incidence small angle X-ray scattering (GISAXS) experiments prove that the structure change in local areas is representative of that over the…