Fabrication and characterization of nanostructured Ni–IrO2 electrodes for water electrolysis
2014
Abstract Nanostructured Ni–IrO2 electrodes were fabricated by electrodeposition in a two-step procedure: first arrays of nickel nanowires (NWs) were electrodeposited within pores of polycarbonate (PC) membranes, then iridium oxide nanoparticles were deposited on the Ni metal after membrane dissolution, for improving the catalytic activity. The aim was to compare performance of these electrodes with traditional ones consisting of Ni film. Different methods of deposition of the IrO2 electrocatalyst were investigated and the effect on electrodes stability and activity is discussed. Despite a low coverage of Ni NWs by the electrocatalyst, results indicate a faster kinetics of O2 evolution in 1 …
CuZnSnSe NANOTUBES AND NANOWIRES BY TEMPLATE ELECTROSYNTHESIS
2014
In this work we present some results of an extensive investigation aimed to find suitable conditions to grow CuZnSnSe (CZTSe) nanostructures through single-step electrodeposition into the channels of polycarbonate membranes. After the optimization of several electrodeposition parameters, we have found that pulsed current deposition, between 0 and -1 mA cm-2, is the best way to obtain CZTSe nanostructures mechanically attached to the support. An interesting result concerns the effect of supporting electrolyte in the deposition bath. In fact, changing its concentration it is possible to vary morphology of nanostructures from nanotubes to nanowires. In both case uniform arrays of ordered nanos…
Amorphous Silicon Nanotubes via Galvanic Displacement Deposition
2013
Amorphous silicon nanotubes were grown in a single step into a polycarbonate membrane by a galvanic displacement reaction conducted in aqueous solution. In order to optimize the process, a specifically designed galvanic cell was used. SEM images, after polycarbonate dissolution, showed interconnected nanotube bundles with an average length of 18 μm and wall thickness of 38 nm.The deposited silicon was revealed by EDS analysis, whilst X-ray diffraction and Raman spectroscopy showed that nanotubes have an amorphous structure. Silicon nanotubes were also characterized by photo-electrochemical measurements that showed n-type conductivity and optical gap of ~1.6 eV. Keywords: Silicon nanotubes, …
Amorphous silicon nanotubes
2017
In the following, the attention will be focused on the silicon nanotube (SiNTs) that is a highly desired form of silicon for its fundamental role in the miniaturization trend of the electronic devices. After a description of the properties and applications of SiNTs and their fabrication methods, the attention will be focused on chemical vapour deposition (CVD) template synthesis that is the most usual synthetic method for this material. Then, galvanic template synthesis will be described as a general method for the fabrication of different metals and oxides nanostructures, therefore the use of this technique for synthesizing SiNTs will be detailed. Characterization methods will be also desc…