M. Baizhumanov
Depth profiles of aggregate centers and nanodefects in LiF crystals irradiated with 34 MeV 84Kr, 56 MeV 40Ar and 12 MeV 12C ions
I. Manika, J. Maniks and R. Zabels acknowledge the national project IMIS2. A. Dauletbekova, A. Akilbekov, M. Zdorovets and A. Seitbayev acknowledge the GF AP05134257of Ministry of Education and Science the Republic of Kazakhstan.
Formation of dislocations and hardening of LiF under high-dose irradiation with 5–21 MeV 12C ions
R. Zabels, I. Manika, J. Maniks, and R.Grants acknowledge the national project IMIS2, and A. Dauletbekova, M. Baizhumanov, and M. Zdorovets the Ministry of Education and Science of the Republic of Kazakhstan for the financial support.
Luminescence of F2 and F3 + centres in LiF crystals irradiated with 12 MeV 12C ions
Dependences of the nanohardness and photoluminescence of F 2 and F 3 + centers on the depth in LiF crystals irradiated with 12 MeV 12 C ions to fluences 10 10 -10 15 ions/cm 2 were studied using laser scanning confocal microscopy, luminescent spectroscopy, and the nanoindentation method. The nanohardness measurements showed a significant hardening effect at the end of the ion run with the dominant contribution of defects formed by the mechanism of elastic collisions. The observed attenuation of the luminescence intensity at high fluences is associated with the intense nucleation of dislocations as traps for aggregate color centers.