Optical absorption and Raman studies of neutron-irradiated Gd3Ga5O12 single crystals
Abstract In this work we have performed a comparative analysis of optical absorption and micro-Raman spectra for series of Gd3Ga5O12 (GGG) single crystals irradiated by fast neutrons with fluences from 1016 n/cm2 to 1018 n/cm2. It was found that the optical absorption spectra of non-irradiated Czochralski grown GGG consist of the relatively narrow lines in the UV spectral range related to the 4f–4f transitions in Gd3+. Transitions from the 6S7/2 ground state to the 6P, 6J and 6D states in a Gd3+ cation are clearly detected. For a GGG crystal containing Ca impurity ions, additional absorption band at 350 nm is observed, and it is tentatively ascribed to oxygen vacancies associated with Ca im…
Time-Resolved Luminescence of Nanocrystalline Inorganic Complex Oxides
Two types of complex nanosized oxides – cerium doped Y3Al5O12 (YAG) and CaWO4– have been studied by means of time-resolved luminescence spectroscopy. Comparative study of time-resolve luminescence characteristics of cerium doped YAG single crystal, nanopowders and nanoceramic as well as for CaWO4 macro- and nanocrystals has been done. Two components in the decay kinetic of Ce3+ related emission in YAG nanocrystals were detected and it was suggested that a different energy transfer rate to volume and surface Ce3+ ions takes place. It is shown that the segregation of Ce3+ ions near nanoparticles surface and/or dislocation lines plays a crucial role in degradation of light yield of cerium rela…