EPR hyperfine structure of F‐type centres in pure LiBaF 3 crystal
We studied EPR spectra of pure LiBaF3 sample of high quality. For EPR measurements LiBaF3 sample was X-irradiated at room temperature, however spectra could be observed at low temperatures - at 77 K. All hyperfine structure lines of F-type centre could be well resolved contrary to our earlier studies of Fe doped LiBaF3 crystal. Qualitative analysis with g-tensor parameters derived from magneto-optical measurements showed that the F-type centre observed earlier by MCD-EPR techniques is the same F-type centre we observe with the EPR. We analyse origin of the hyperfine structure of the EPR spectra and their angular dependencies and discuss the structure of F-type centres in the LiBaF3 crystal.…
Magnetooptical studies of defects and recombination luminescence in LiBaF3
Abstract Optically detected EPR investigations have been performed on the recombination luminescence (RL-EPR) of LiBaF3 crystal, X-irradiated at T=4.2 K . RL-EPR lines of VK- centres were found, as well as further lines of a defect with S= 1 2 and an axial g-tensor with its main axis along a [1 0 0] direction of the crystal. Measurements of the magnetic circular dichroism of the absorption (MCDA) have been performed on LiBaF3 crystals X-irradiated at two temperatures ( 4.2 K and RT). After irradiation at T=4.2 K , the main MCDA bands peak at 453 and 500 nm , but after irradiation at T=300 K , the main bands peak at 444 and 390 nm , there is a change of the sign between the peaks in both cas…
Thermostimulated recombination processes in LiBaF3 crystals
Abstract The creation of radiation defects in LiBaF 3 crystals at 10 K and the processes of their thermostimulated recombination are investigated. The methods of optical absorption, thermal bleaching of color centers, thermostimulated luminescence and fractional glow technique are used. The radiation defects anneal in a multi-stage process accompanied with thermo-luminescence at 20, 46, 105, 130, 170, 210 and 270 K . Differences in the optical absorption spectra measured before and after the TSL peaks are obtained and recombination parameters are determined. The TSL peak at 20 K arises from the delocalization of H-centers. The presence of two TSL peaks related to V K -centers at 105 and 130…