Chen Song
Deposition of binder-free oxygen-vacancies NiCo2O4 based films with hollow microspheres via solution precursor thermal spray for supercapacitors
Abstract Hollow micro-/nanostructures and oxygen vacancies are highly desirable for supercapacitors due to high active surface area and outstanding electrochemical properties. In order to benefiting from the both effect, binder-free oxygen-vacancies NiCo2O4 based films with hollow microspheres were pioneering directly deposited via one kind thermal spray technology, named solution precursor thermal spray (SPTS) process. To our best knowledge, the rapid one-step SPTS route was firstly employed to synthesize and deposit NiCo2O4 films for supercapacitor applications. The CV data clearly demonstrated that the specific capacitances of more oxygen-deficient NiCo2O4 electrodes with hollow microsph…
Oxygen-deficient Co3O4 submicron porous sphere films as highly active supsercapacitor electrodes
Abstract Herein, we report Co3O4 films with different content of oxygen vacancies and shapes of particles for supercapacitor electrodes. Under the similar area ratio of OII peak in the XPS spectrum of oxygen elements, the specific capacitance of electrode films with hollow spongy-like particles (963 F/g under a scan rate of 5 mV/s) is 1.6 times higher than that of the electrodes with solid irregular particles (596 F/g), indicating the effect of particle shapes on electrochemical properties. The films composed of submicron porous spheres and containing highest content of oxygen vacancies exhibited the specific capacitances as high as 1700 F/g under the scan rate of 5 mV/s. By contrast, after…
New preparation of ceramic coatings by low-pressure plasma spray
As an advanced thermal spray technology, low-pressure plasma spray (LPPS) allows obtaining high-quality coatings and can bridge the thickness gap between conventional thermal spray technologies and standard thin film processes. Moreover, LPPS permits to build uniform coatings with various microstructures; deposition takes place not only from liquid splats but also from nano-sized clusters as well as from the vapor phase depending on operational conditions. In order to further improve and develop the LPPS process, this research aims to combine it with the emerging suspension plasma spray and reactive plasma spray processes. It was expected to both provide two novel integrated processes and a…