Imaging of current induced Néel vector switching in antiferromagnetic Mn 2 Au
The effects of current induced N\'eel spin-orbit torques on the antiferromagnetic domain structure of epitaxial Mn$_2$Au thin films were investigated by X-ray magnetic linear dichroism - photoemission electron microscopy (XMLD-PEEM). We observed current induced switching of AFM domains essentially corresponding to morphological features of the samples. Reversible as well as irreversible N\'eel vector reorientation was obtained in different parts of the samples and the switching of up to 30 % of all domains in the field of view of 10 $\mu$m is demonstrated. Our direct microscopical observations are compared to and fully consistent with anisotropic magnetoresistance effects previously attribu…
Magnetoresistance effects in the metallic antiferromagnet Mn$_2$Au
In antiferromagnetic spintronics, it is essential to separate the resistance modifications of purely magnetic origin from other effects generated by current pulses intended to switch the N\'eel vector. We investigate the magnetoresistance effects resulting from magnetic field induced reorientations of the staggered magnetization of epitaxial antiferromagnetic Mn2Au(001) thin films. The samples were exposed to 60 T magnetic field pulses along different crystallographic in-plane directions of Mn2Au(001), while their resistance was measured. For the staggered magnetization aligned via a spin-flop transition parallel to the easy [110]-direction, an ansiotropic magnetoresistance of -0.15 % was m…