An Approach on the Hydrogen Absorption in Carbon Black after Gamma Irradiation
In this work, different samples of an industrial carbon black are used to study the hydrogen intake from an over pres-surized atmosphere and its changes due to alteration of its level of crystallinity produced by ¿-irradiation. The monitor-ing of the hydrogen adsorption was made by means of thermogravimetric analysis and by measurements of some elec-trical parameters as the Seebeck coefficient. X-ray diffraction shows that the irradiation diminishes the level of crystal-line perfection. These results show interesting possibilities to use carbon black as cheap hydrogen absorbers.
Effects of Gamma Irradiation on the Kinetics of the Adsorption and Desorption of Hydrogen in Carbon Microfibres
In this study, three types of carbon fibres were used, they were ex-polyacrylonitrile carbon fibres with high bulk modulus, ex-polyacrylonitrile fibres with high strength, and vapour grown carbon fibres. All the samples were subjected to a hydrogen adsorption process at room temperature in an over-pressured atmosphere of 25 bars. The adsorption process was monitored through electrical resistivity measurements. As conditioning of the fibres, a chemical activation by acid etching followed by ¿-ray irradiation with 60Co radioisotopes was performed. The surface energy was deter-mined by means of the sessile drop test. Both conditioning treatments are supplementary; the chemical activation works…