Multiband light emission and nanoscale chemical analyses of carbonized fumed silica
Fumed silica with a specific area of 295 m2/g was carbonized by successive phenyltrimethoxysilane treatments followed by annealing in inert atmosphere up to 650 °C. Emission, excitation, kinetics, and photo-induced bleaching effects were investigated by steady state and time-resolved photoluminescence spectroscopies. The local chemistry was also studied by infrared transmission spectroscopy. Strong ultraviolet and visible photoluminescence was observed in the samples after the chemical treatments/modifications and thermal annealing. It has been shown that ultraviolet photoluminescence in chemically modified fumed silica is associated with phenyl groups, while near ultraviolet and visible em…
Effect of Hydration Procedure of Fumed Silica Precursor on the Formation of Luminescent Carbon Centers in SiO 2 :C Nanocomposites
The effect of hydration procedure of fumed silica precursor on photoluminescent properties of carbonized silica (SiO2:C) nanocomposite after chemo/thermal treatments is studied. Main structural effect is the formation of chemical bonding of phenyl groups to silica surface via multiple CSiO bonding bridges. Synthesized samples demonstrate very broad photoluminescence (PL) bands in near ultraviolet and visible ranges with maximum intensity dependent on temperature of thermal annealing. Two main trends in luminescence properties are: 1) hydration-induced blue shift of PL in comparison with PL of unhydrated series; 2) red shift of PL bands with increasing synthesis temperature regardless hydr…