Thin epitaxial films of the Heusler compound

2005

Abstract We prepared thin films of the Heusler compound Co 2 Cr 0.6 Fe 0.4 Al with the B2 structure on a-plane (1 1  2 ¯  0) Al 2 O 3 by sputtering. Films grown at high temperatures ( T ⩾ 600 ∘ C ) on Al 2 O 3 are fully epitaxial with the (1 1 0) and (1  1 ¯  0) planes of the film parallel to the (1 1  2 ¯  0) and (0 0 0 1) planes of the substrate, respectively. These epitaxial films possess a higher surface roughness than films grown at room temperature. The films show nearly rectangular hysteresis loops with coercive fields of the order of 10 mT. Magnetooptical Kerr measurements show an in-plane anisotropy of the magnetization with the easy axis in { 0 0 1 } direction. Hall measurements s…