Particle size-related limitations of persistent phosphors based on the doped Y3Al2Ga3O12 system
AbstractCo-doped Ce3+, Cr3+ and Pr3+ yttrium–aluminium–gallium garnet powders of various sizes were obtained by co-precipitation method. The microstructure and morphology were investigated by XRPD, TEM and gas porosimetry. The luminescence properties were studied by excitation and emission spectra, quantum yield and decay times. Thermoluminescence measurements were performed to evaluate the activation energy, traps redistribution and frequency factor. Limitation in the energy transfer between dopant ions in the small particles, traps depth and surface defects were considered and investigated as responsible for the quenching of persistent luminescence. The phosphors annealed at 1100 °C show …
Effect of annealing temperature on persistent luminescence of Y3Al2Ga3O12:Cr3+ co-doped with Ce3+ and Pr3+
Abstract Y3(Al,Ga)5O12 (YAGG) materials doped with Ce3+, Cr3+ and Pr3+ were synthesized by using a modified Pechini method and subsequently annealed in air at selected temperatures between 900 and 1500 °C. According to X-ray powder diffraction (XRPD) and transmission electron microscopy (TEM) analyses, the particles and size distributions become large and broad, respectively, due to sintering and agglomeration at high annealing temperatures. Based on infrared (FTIR) spectra and calculation of multi-phonon de-excitation probabilities, the high energy O–H vibrations are not causing significant multi-phonon de-excitation of the emitting 5d level of Ce3+ if the annealing temperature is above 90…
Effect of annealing treatment on the persistent luminescence of Y3Al2Ga3O12:Ce3+,Cr3+,Pr3+ ceramics
Abstract The Y3Al2Ga3O12:Ce3+,Cr3+,Pr3+ (YAGG) persistent luminescent ceramics were sintered in static air (without airflow) and followed by hot isostatic pressing (HIP) treatment. The low aggregated and relatively narrow particle-size distributed starting powders, with the particle size of about 50 nm, were synthesized by using Pechini method and then annealed at 900 °C for 16 h in static air. Compared to nano-phosphors, the ceramics exhibited more intense and longer persistent luminescence (PersL). The photoluminescence and PersL spectra were found to have a similar shape, indicating that the emitting centers for photoluminescence and PersL processes were same. The intense Ce3+ and Cr3+ b…
Optical studies of Y3(Al,Ga)5O12:Ce3+,Cr3+,Nd3+ nano-phosphors obtained by the Pechini method
The Y-3(Al,Ga)(5)O-12:Ce3+,Cr3+,Nd3+ (YAGG) nano-phosphors with homogeneous particle-size distribution, low aggregation and average crystalline size of about 65 nm were obtained using a modified Pechini method. Only slight aggregation of the crystallites occurs after post-annealing at 1100 degrees C. The intense Ce3+ bands in the excitation spectra of the Ce3+,Cr3+,Nd3+ co-doped materials monitoring the Cr3+ emission at 690 nm indicate energy transfer from Ce(3+ )to Cr3+. Weak Nd3+ lines are observed, as well. In addition, the emission of Nd3+ at 1060 nm with excitation of Ce3+ and Cr3+ confirms the Ce3+/Cr3+ to Nd3+ energy transfer. The short average luminescence decay times for the Ce3+ e…