Kinetics of Bulk Lifetime Degradation in Float‐Zone (FZ) Silico n : Fast Activation and Annihilation of Grown‐In Defects and the Role of Hydrogen vs Light

Float-zone (FZ) silicon often has grown-in defects that are thermally activated in a broad temperature window (≈300–800 °C). These defects cause efficient electron-hole pair recombination, which deteriorates the bulk minority carrier lifetime and thereby possible photovoltaic conversion efficiencies. Little is known so far about these defects which are possibly Si-vacancy/nitrogen-related (VxNy). Herein, it is shown that the defect activation takes place on sub-second timescales, as does the destruction of the defects at higher temperatures. Complete defect annihilation, however, is not achieved until nitrogen impurities are effused from the wafer, as confirmed by secondary ion mass spectro…