Structure of nanoporous carbon materials for supercapacitors
Activated carbons with highly developed porous structure and nanosized pores (8 - 11 A) were prepared from alder wood using thermochemical activation method with sodium hydroxide. Properties of the obtained activated carbons were examined by benzene and nitrogen sorption, X-Ray diffraction and Raman spectroscopy. Tests of activated carbons as electrodes in supercapacitors were performed as well. It was found that specific surface area of above mentioned activated carbons was 1800 m 2 /g (Dubinin - Radushkevich). Raman spectroscopy demonstrated the presence of ordered and disordered structures of graphite origin. The performance of activated carbons as electrodes in supercapacitors have show…
Highly Porous Wood Based Carbon Materials for Supercapacitors
Wood based activated carbons synthesized by two-stage thermocatalytical synthesis with NaOH activator were studied and used as supercapacitor electrodes (sulphuric acid electrolyte). Porous structure and electrochemical properties of carbons vs synthesis conditions were assessed. It was found that there are correlations between carbons synthesis variables, their porosity and supercapacitors functional characteristics. At the temperature 600 o C and activator/precursor ratio 1.25 porosity decreased, however energy capacitance of supercapacitor increased calculating on elementary cell mass.