Effect of annealing temperature on persistent luminescence of Y3Al2Ga3O12:Cr3+ co-doped with Ce3+ and Pr3+
2021
Abstract Y3(Al,Ga)5O12 (YAGG) materials doped with Ce3+, Cr3+ and Pr3+ were synthesized by using a modified Pechini method and subsequently annealed in air at selected temperatures between 900 and 1500 °C. According to X-ray powder diffraction (XRPD) and transmission electron microscopy (TEM) analyses, the particles and size distributions become large and broad, respectively, due to sintering and agglomeration at high annealing temperatures. Based on infrared (FTIR) spectra and calculation of multi-phonon de-excitation probabilities, the high energy O–H vibrations are not causing significant multi-phonon de-excitation of the emitting 5d level of Ce3+ if the annealing temperature is above 90…
Effect of surface impurities on downconversion luminescence of Pr3+, Yb3+ activated SrF2 nanoparticles
2020
Abstract Pr3+,Yb3+ activated SrF2 nanoparticles synthesized by low-temperature hydrothermal method were studied. The composition and size of nanoparticles were intentionally changed by controlling synthesis conditions. After structural and morphological characterization, the spectroscopic properties of the nanoparticles were analyzed in the visible and near infrared spectra ranges. The results show correlation between the gradual change of the amount of carboxylate and hydroxyl moieties on the nanoparticle surface, varied by the size nanoparticles and the quenching of the luminescence. The size-related amount of surface quenchers is strongly connected to the decrease of the downconversion e…
Effect of annealing treatment on the persistent luminescence of Y3Al2Ga3O12:Ce3+,Cr3+,Pr3+ ceramics
2020
Abstract The Y3Al2Ga3O12:Ce3+,Cr3+,Pr3+ (YAGG) persistent luminescent ceramics were sintered in static air (without airflow) and followed by hot isostatic pressing (HIP) treatment. The low aggregated and relatively narrow particle-size distributed starting powders, with the particle size of about 50 nm, were synthesized by using Pechini method and then annealed at 900 °C for 16 h in static air. Compared to nano-phosphors, the ceramics exhibited more intense and longer persistent luminescence (PersL). The photoluminescence and PersL spectra were found to have a similar shape, indicating that the emitting centers for photoluminescence and PersL processes were same. The intense Ce3+ and Cr3+ b…
Optical studies of Y3(Al,Ga)5O12:Ce3+,Cr3+,Nd3+ nano-phosphors obtained by the Pechini method
2019
The Y-3(Al,Ga)(5)O-12:Ce3+,Cr3+,Nd3+ (YAGG) nano-phosphors with homogeneous particle-size distribution, low aggregation and average crystalline size of about 65 nm were obtained using a modified Pechini method. Only slight aggregation of the crystallites occurs after post-annealing at 1100 degrees C. The intense Ce3+ bands in the excitation spectra of the Ce3+,Cr3+,Nd3+ co-doped materials monitoring the Cr3+ emission at 690 nm indicate energy transfer from Ce(3+ )to Cr3+. Weak Nd3+ lines are observed, as well. In addition, the emission of Nd3+ at 1060 nm with excitation of Ce3+ and Cr3+ confirms the Ce3+/Cr3+ to Nd3+ energy transfer. The short average luminescence decay times for the Ce3+ e…
Urea Glass Route as a Way to Optimize YAGG:Ce3+,Cr3+,Pr3+ Nanocrystals for Persistent Luminescence Applications
2022
A new approach for the synthesis of Y3Al2Ga3O12 (YAGG) nanophosphors allowing the preparation of crystallites with sizes starting from 45 nm is presented. The controllability of the energy and trap density of the resulting material samples by annealing temperature was confirmed by thermoluminescence (TL) measurements. It has been shown that the annealing of samples at temperatures up to 1300 degrees C does not cause any substantial growth of crystallites, still remaining below 100 nm, but leads to changes in the activation energy of the persistent luminescence (PersL) process. On the other hand, annealing above 1400 degrees C results in grain growth on the submicron scale, which was confirm…