Formation of anodic films on sputtering-deposited Al–Hf alloys

Abstract The growth of barrier-type anodic films at high efficiency on a range of sputtering-deposited Al–Hf alloys, containing from 1 to 95 at.% Hf, has been investigated in ammonium pentaborate electrolyte. The alloys encompassed nanocrystalline and amorphous structures, the latter being produced for alloys containing from 26 to 61 at.% Hf. Except at the highest hafnium content, the films were amorphous and contained units of HfO 2 and Al 2 O 3 distributed relatively uniformly through the film thickness. Boron species were confined to outer regions of the films. The boron distributions suggest that the cation transport number decreases progressively with increasing hafnium concentration i…