Unusual stoichiometry control in the atomic layer deposition of manganese borate films from manganese bis(tris(pyrazolyl)borate) and ozone
The atomic layer deposition (ALD) of films with the approximate compositions Mn3(BO3)2 and CoB2O4 is described using MnTp2 or CoTp2 [Tp ¼ tris(pyrazolyl)borate] with ozone. The solid state decomposition temperatures of MnTp2 and CoTp2 are 370 and 340 C, respectively. Preparative-scale sublimations of MnTp2 and CoTp2 at 210 C/0.05 Torr afforded >99% recoveries with <0.1% nonvolatile residues. Self-limited ALD growth was demonstrated at 325 C for MnTp2 or CoTp2 with ozone as the coreactant. The growth rate for the manganese borate process was 0.19 A˚ /cycle within the ALD window of 300–350 C. The growth rate for the cobalt borate process was 0.39–0.42 A˚ /cycle at 325 C. X-ray diffraction of …
Low Temperature Growth of High Purity, Low Resistivity Copper Films by Atomic Layer Deposition
The atomic layer deposition of copper metal thin films was achieved using a three precursor sequence entailing Cu(OCHMeCH2NMe2)2, formic acid, and hydrazine. A constant growth rate of 0.47−0.50 A/cycle was observed at growth temperatures between 100 and 170 °C. The resulting films are high purity and have low resistivities.