Raman spectra of (PbS)1.18(TiS2)2 misfit compound

2007

Abstract A Raman study on the (PbS)1.18(TiS2)2 semiconductor structure with incommensurate layers (misfit) is reported. The different bands observed in the spectra are attributed to both the TiS2 host layers, at 219 (Eg) and 333 (A1g) cm−1, and the intercalated PbS layers: the LO(Γ), 2LO and 3LO phonons at 203, 412 and 634 cm−1, respectively. A phonon peak probably related to the superposition of TiS2 and PbS vibrations, was observed near 286 cm−1. The decrease of the phonon wave numbers (of the modes located at 203, 333, 412, and 634 cm−1) with increasing laser power pointed out negative temperature coefficients of these modes. A peak appearing with laser power near 151 cm−1 is discussed. …