<title>Primary radiation defect formation in silver halides</title>
Donats MillersLarisa Grigorjevasubject
Crystallographychemistry.chemical_compoundMaterials scienceSilver halidechemistryPhononExcitonHalidePhysical chemistryIrradiationAbsorption (chemistry)LuminescenceSolid solutiondescription
Under irradiation the formation of primary intrinsic defects in silver halide solid solutions AgBr1-xClx take place via strong exciton-phonon interaction. Efficiency of these defects formation depend on solid solution composition and within 0 <EQ x <EQ 0.15 dependence on temperature was observed too. Estimation shows efficiency of defects creation is approximately 0.01 for AgCl and noticeably higher for AgBr.© (1998) COPYRIGHT SPIE--The International Society for Optical Engineering. Downloading of the abstract is permitted for personal use only.