The effect of incorporating different concentrations of chlorhexidine digluconate on the degree of conversion of an experimental adhesive resin

subject

description

Background The aim of this study was to evaluate the effect of chlorhexidine digluconate incorporation on the degree of conversion of an experimental adhesive resin. Material and Methods The experimental resin was prepared from 70 wt% bisphenol A glycerolate dimethacrylate, 30 wt% hydroxyethyl methacrylate, silanized SiO2 nanofillers, 0.5% of camphorquinone and ethyl 4-dimethylaminebenzoate (binary photo-initiator system). Five chlorhexidine digluconate concentrations (0, 0.5, 1, 2 and 4 wt%) were then incorporated into the experimental resin. Thirty Potassium Bromide pellets were prepared then divided into six groups (n=5/group), repre¬senting the tested adhesive resins (Single Bond 2, 0, 0.5, 1, 2 and 4 wt% chlohexidine-incorporated experimental adhesive resins), that were applied to the pellets without light-curing (uncured specimens). Another 30 pellets were prepared and treated with the previous materials then light-cured using LED light-curing device (cured specimens). Degree of conversion of the uncured and the cured specimens were evaluated using FTIR analysis. Results Adper Single Bond 2 showed the highest degree of conversion mean values followed by 0.5 wt% chlorhexidine concentration then 2 wt% followed by 4 wt% then 1 wt% concentrations, while 0 wt% concentration showed the lowest mean values. Conclusions Chlorhexidine digluconate had slight significant influence on the efficiency of polymerization of the experimental adhesive resin. Key words:Chlorhexidine digluconate, different concentrations, degree of conversion, experimental adhesive resin.