Solubility and pH of bioceramic root canal sealers: A comparative study

subject

description

Background This study compared the solubility and the pH of different root canal sealers in vitro. Material and Methods BioRoot™RCS, TotalFill BC Sealer, MTA Fillapex, SealapexTM, AH Plus, EasySeal, Pulp Canal Sealer™ and N2 were tested. Similar specimens were prepared using ring molds with an internal diameter of 20 ± 0,1 mm and a height of 1,5 ± 0,1 mm and digitally weighted to register the mass of each specimen before and after immersion in distilled water. Solubility was determined after 24 hours and statistically analysed using a one-way ANOVA test and post-hoc Tukey test. The pH value was measured by a digital pH meter after 3 and 24 hours from manipulation. Results BioRoot™RCS and TotalFill BC Sealer showed significantly higher solubility (P<0.05). All the remnant root canal sealers fulfilled the requirements of solubility of the International Standard Organization 6876 demonstrating a weight loss of less than 3%. BioRoot™RCS and Totalfill BC Sealer exhibited high alkaline pH over time (P<0.05); the alkalinity of the other tested cements was significantly lower. Conclusions The prolonged alkalinity of bioceramic sealer matched the increase in solubility. This may encourage their biological and antimicrobial effects, but the ongoing solubility may impact their ability to prevent apical leakage. Key words:pH, root canal sealers, solubility.