F-centre luminescence in nanocrystalline CeO2

subject

description

Nanocrystalline CeO2 powders were synthesized by two cost-effective methods: the self-propagating room temperature (SPRT) method and the precipitation method. Differently prepared samples exhibited different temperature-dependent photoluminescence (PL) in the ultraviolet and visible regions. The PL signals originated from different kinds of oxygen-deficient defect centres with or without trapped electrons (F0, F+ or F++ centres). The temperature-dependent PL spectra were measured using different excitation lines, below (457, 488 and 514?nm) or comparable (325?nm) to the ceria optical band gap energy, in order to investigate the positions of intragap localized defect states. Evidence for the presence of F+ centres was supported by the signals observed in electron paramagnetic resonance (EPR) measurements. Based on PL and EPR measurements it was shown that F+ centres dominate in the CeO2 sample synthesized by the SPRT method, whereas F0 centres are the major defects in the CeO2 sample synthesized by the precipitation method. The luminescence from F++ states, as shallow trap states, was registered in both samples. Energy level positions of these defect states in the ceria band gap were proposed.