Ultimate tensile properties and dart impact behaviour of coextruded films of LDPE and LLDPE were compared with those of films made from blends of the same resins. The effect of composition and of both blow up ratio and axial draw ratio of the blowing process on film properties was explored. The results indicate that, at least for semicompatible systems like that considered here, films made from blends and coextruded ones have mechanical properties very close to each other. Die Festigkeitseigenschaf ten und das Verhalten beim Kugelfalltest von coextrudiertcn Filmen aus LDPE und LLDPE wurden mit den entsprechenden Eigenschaften von aus Mischungen dieser Polymere hergestellten Filmen verglichen. Der Einflus der Zusammensetzung, des Aufblasverhaltnisses und des achsialen Reckverhaltnisses auf die Filmeigeneigenschaften wurde untersucht. Die Ergebnisse zcigen, das zumindest bei den hicr betrachteten semivertraglichen Systemen die Eigensehaften der durch Coextrusion bzw. aus dem Polymergemisch bergestellten Filme dicht beieinander liegen.
| year | journal | country | edition | language |
|---|---|---|---|---|
| 1986-11-01 | Acta Polymerica |