45 g of poly(acrylic acid) (PAA 500) with a trimodal molar mass distribution (Mw = 500 kg/mol, (Mw/Mn) −1 = 2.33) were fractionated by means of CPF (continuous polymer fractionation) in two steps using 1,4-dioxane as solvent. The counter-current extraction was performed in a glass column (length: 190 cm, diameter: 1.5 cm) filled with a network of wires, introducing the feed 75 cm from its upper end. The distribution of the highest molar mass fraction (Mw = 760 kg/mol) is unimodal and comparatively narrow ((Mw/Mn) −1 = 0.66). Indications exits that fractionation is not only taking place with respect to molar mass but also with respect to tacticity. Mit Hilfe der kontinuierlichen Polymerfraktionierung (CPF) wurden 45 g Poly(acrylsaure) (PAA 500) mit einer trimodalen Molmassenverteilung (Mw = 500 kg/mol, (Mw/Mn) −1 = 2,33) in zwei Stufen mit 1,4-Dioxan als Losungsmittel fraktioniert. Die Gegenstrom-Extraktion wurde in einer Glaskolonne (Lange: 190 cm, Durchmesser: 1,5 cm) durchgefuhrt, die mit einem Drahtnetzwerk gefullt war, indem die Losung 75 cm vom oberen Ende zugefuhrt wurde. Die Verteilung der Fraktion mit der hochsten Molmasse (Mw = 760) ist unimodal und vergleichsweise eng ((Mw/Mn) −1 = 0,66). Es bestehen Anhaltspunkte, das die Fraktionierung nicht nur in bezug auf die Molmasse, sondern auch in bezug auf die Taktizitat erfolgt.