Über die autoxydation des syndiotaktischen polypropylens
1964
Bei der Autoxydation des syndiotaktischen Polypropylens in Losung lost ein monofunktioneller Zerfall der entstehenden Hydroperoxidgruppen den Kettenstart und die Autokatalyse der Radikalkettenreaktion aus. Die Ergebnisse bestatigen die Vorstellungen uber den Aufbau syndiotaktischer Polymer. Mit Hilfe der Autoxydation ist eine Unterscheidung zwischen syndiotaktischem und isotaktischem Polypropylen moglich. Chain initiation and autocatalysis of the radical chain reaction in the autoxidation of syndiotactic polypropylene is produced by the monofunctional decomposition of the hydroperoxide groups formed. The results confirm the conceptions on the structure of syndiotactic polymers. Autoxidation…
Evaluation of molecular mass and tacticity of polyvinyl alcohol by non-equilibrium capillary electrophoresis of equilibrium mixtures of a polymer and…
2011
Non-equilibrium capillary electrophoresis of equilibrium mixtures (NECEEM) has been used to characterize polyvinyl alcohol (PVA). Commercial PVA samples with different molecular masses, from M(w)=15 up to 205 kDa, were used. According to the (13)C NMR spectra, the samples also differed in tacticity (stereoregularity). Mixtures of PVA and the anionic azo-dye Congo Red (CR) were injected in the presence of a borate buffer. The electropherograms gave a band and a peak due to the residual PVA-CR complex and the excess dye, respectively, plus a superimposed exponential decay due to the partial dissociation of the complex during migration. The stoichiometry of the PVA-CR complex, q=[monomer]/[dye…
Wide-range cooling characteristics of a selected isotactic polypropylene
1997
Abstract An increased knowledge of polymer crystallization kinetics and its effect on the crystalline structure is of particular importance at high cooling rates. The aims of this study were to explore the range of utility and complementarity of various methods (densitometry, microscopy, wide-angle x-ray diffraction [WAXD], and small-angle light scattering [SALS]) on the characterization of the crystalline structure of a high purity isotactic polypropylene (PP) in a wider cooling range than previously obtainable and to identify characteristic ranges of the structure as a function of cooling rate. High cooling rates, ranging to nearly 1000°C/sec, were obtained using a special quench device. …
Crystallization kinetics of iPP: Influence of operating conditions and molecular parameters
2007
An analysis of the crystallization kinetics of different grades of isotactic polypropylene (iPP) is here presented. To describe the crystallization kinetics as a function of molecular and operating parameters, the methodological path followed was the preparation of quenched samples of known cooling histories, calorimetric crystallization isotherms tests, differential scanning calorimetry cooling ramps, wide angle X-ray diffraction (WAXD) measurements, and density determination. The WAXD analysis performed on the quenched iPP samples confirmed that during the fast cooling at least a crystalline structure and a mesomorphic one form. The diffractograms were analyzed by a deconvolution procedur…
Solidification of syndiotactic polystyrene by a continuous cooling transformation approach
2007
Syndiotactic polystyrene (sPS) was solidified from the melt under drastic conditions according to a continuous cooling transformation methodology developed by the authors, which covered a cooling rate range spanning from approximately 0.03 to 3000 °C/s. The samples produced, structurally homogeneous across both their thickness and surface, were analyzed by macroscopic methods, such as density, wide-angle X-ray diffraction (WAXD), and microhardness (MH) measurements. The density was strictly related to the phase content, as confirmed by WAXD deconvolution. The peculiar behavior encountered (the density first decreasing and then increasing with the cooling rate) was attributed to the singular…
An experimental methodology to study polymer crystallization under processing conditions. The influence of high cooling rates
2002
Abstract A new experimental route for investigating polymer crystallization under very high cooling rates (up to 2000°C/s) is described. A complete and exhaustive description of the apparatus employed for preparing thin quenched samples (100– 200 μm thick) is reported, the cooling mechanism and the temperature distribution across sample thickness is also analysed, showing that the final structure is determined only by the thermal history imposed by the fast quench apparatus. Details concerning the characterization techniques used to probe the final structure are reported, including density measurements and wide angle X-ray diffraction patterns. Experimental results concerning isotactic poly…
Isotactic polypropylene solidification under pressure and high cooling rates. A master curve approach
2000
Solidification in industrial processes very often involves flow fields, high thermal gradients and high pressures: the development of a model able to describe the polymer behavior becomes complex. Recently a new equipment has been developed and improved to study the crystallization of polymers when quenched under pressure. An experimental apparatus based on a modified, special injection moulding machine has been employed. Polymer samples can be cooled at a known cooling rate up to 100 °C/s and under a constant pressure up to 40 MPa. Density, Micro Hardness (MH), Wide angle X-ray diffraction (WAXD), and annealing measurements were then used to characterize the obtained sample morphology. Res…
Competition between α and γ phases in isotactic polypropylene: effects of ethylene content and nucleating agents at different cooling rates
2001
Abstract The influence of ethylene content, nucleating agents and cooling rate upon the formation of γ phase in isotactic polypropylene is investigated. Detailed analysis of wide angle X-ray diffraction shows that some γ phase can appear even in copolymers of very low ethylene content (0.5 mol.%). Differential scanning calorimetry shows a double melting peak. Nucleating agents of different types are found to enhance γ phase crystallization, even in high molecular weight homopolymers. In any of the materials studied the amount of γ phase decreases with increasing cooling rate, going to zero at a cooling rate of about 10°C s−1. We interpret the observations in terms of the kinetics of growth …
1986
Mechanical properties of blends of low density polyethylene with isotactic polypropylene II. effect of mixing temperature and rate
1989
Abstract The effects of mixing temperature and rate on tensile properties of some blends of low density polyethylene with isotactic polypropylene have been studied. Results, with those presented previously on the effect of mixing time, indicate significant effects of mixing parameters and suggest the need to find an “optimum mixing procedure” for each kind of blend.