The stress relaxation behaviour after compression yielding of two semicrystalline polymers, a low density polyethylene and an isotactic polypropylene, is investigated. Data taken at several strains, reached with different sample loading rates, are considered. Master curves are obtained by means of dimensionless stress and time measures, similar to those recently adopted for some amorphous polymers. Die Spannungsrelaxation nach Druckbeanspruchung wurde an zwei semikristallinen Polymeren, Polyethylen neidriger Dichte und isotaktischem Polypropylen, untersucht. Die bei unterschiedlichen Deformationen, welche mit unterschiedlichen Beanspruchungsgeschwindigkeiten erreicht wurdern, erhaltenen Ergebnisse werden diskutiert. Durch Einfuhrung dimensionsloser Spannungs- und Zeit-Mase wurden Masterkurven erhalten, ahnlich wie fruher bei einigen amorphen Polymeren.
| year | journal | country | edition | language |
|---|---|---|---|---|
| 1982-12-01 | Acta Polymerica |