Effect of different adhesive strategies on the microtensile bond strength of dentin to indirect resin-based composite.

subject

description

Background To evaluate the microtensile bond strength of indirect resin composite bonded to dentin using five different adhesives strategies. Material and Methods Forty specimens (Solidex) were produced and randomly into five groups with different adhesives strategies: (G1)- Single Bond Universal + etch + silane + RelyX Ultimate, (G2)- Single Bond Universal + silane + RelyX Ultimate, (G3)- Single Bond Universal + etch + RelyX Ultimate, (G4)- Single Bond Universal + RelyX Ultimate, and (G5)-Scotchbond Multi-purpose + RelyX ARC. After cementation the specimens were stored in 100% humidity for 24hours at 37°C. The specimens were sectioned perpendicular to the adhesive interface to obtain beams and submitted to microtensile test. Microtensile values were expressed in MPa and analyzed by one-way ANOVA and multiple comparison Tukey tests (α=0.05). Results The mean bond strength in MPa groups were: G1=11,48, G2=14,15, G3=16,95, G4=17,03 and G5=16,80. Statistical analysis showed that the bond strength values were not significantly affected by the different adhesive strategies. Conclusions Cementation of dentin to indirect resin composite cannot be significantly affected by different adhesive strategies used. The specimens treated with silane, etch associated with Single bond universal did not increase bond strength values. Key words:Adhesives, dental cements, dentin.