In situ— High Temperature Mössbauer Spectroscopy of Iron Nitrides and Nitridoferrates

subject

description

The stoichiometric iron nitrides γ′-Fe4N, e-Fe3N and ζ-Fe2N were characterized by Mossbauer spectroscopy. The thermal decomposition of e-Fe3N was studied in-situ by means of a specially developed Mossbauer furnace. We found e-Fe3N to γ′-Fe4N and e-Fe3Nx (x ≥ 1.3) as decomposition products and determined the border of γ′/e transformation at T ≅ 930 K. Mossbauer spectroscopy was applied to study in-situ the thermal decomposition of the nitridometalate Li3[FeIIIN2] and the formation of Li2[(Li1-xFeIx)N], the compound with the largest local magnetic field ever observed in an iron containing material. The kinetics of formation and the stability of Li2[(Li1-xFeIx)N] was of particular interest in the present study. In-situ — Hoch-Temperatur Mossbauer Spectroskopie von Eisennitriden und Nitridoferraten Die stochiometrischen Eisennitride γ′-Fe4N, e-Fe3N und ζ-Fe2N wurden mittels Mossbauer-Spektrospkopie charakterisiert. Die thermische Zersetzung von e-Fe3N wurde mit Hilfe eines speziell entwickelten Mossbauer-Ofens untersucht. Wir erhielten γ′-Fe4N und e-Fe3Nx (x ≥ 1, 3) als Zersetzungsprodukte und konnten die Grenze der Umwandlung γ′/e zu etwa T = 930 K festlegen. Die Mossbauer-Spektroskopie wurde auch zur Untersuchung der thermischen Zersetzung des Nitridometallates Li3[FeIIIN2] in-situ angewendet, wobei Li2[(Li1-xFeIx)N] entsteht, die Verbindung mit dem grosten lokalen Magnetfeld, das jemals beobachtet wurde. Die Bildungskinetik und die Stabilitat von Li2[(Li1-xFeIx)N] waren dabei von besonderem Interesse in der vorliegenden Arbeit.