A microstructural model for homogenisation and cracking of piezoelectric polycrystals
2019
Abstract An original three-dimensional generalised micro-electro-mechanical model for computational homogenisation and analysis of degradation and micro-cracking of piezoelectric polycrystalline materials is proposed in this study. The model is developed starting from a generalised electro-mechanical boundary integral representation of the micro-structural problem for the individual bulk grains and a generalised cohesive formulation is employed for studying intergranular micro-damage initiation and evolution into intergranular micro-cracks. To capture the electro-mechanical coupling at the evolving damaging intergranular interfaces, standard mechanical cohesive laws are enriched with suitab…
Early-stage detection of surface stress corrosion cracking at the subgranular level
2014
The strain field at the interface between an alloy and its oxide layer has been mapped using nanopatterned gauges resistant to the environment of the primary nuclear medium. It was found that oxidation has decreased the alloy ductility, thereby enabling some grain boundary opening to be detectable from 1.8 % strain. It is shown that statistics of extreme rare events of hotspots quantify the occurrence of the local opening of intergranular cracks, and thereby the ageing process.
Grain-boundary modelling of hydrogen assisted intergranular stress corrosion cracking
2018
Abstract A novel hybrid strategy for modelling intergranular hydrogen embrittlement in polycrystalline microstructures is proposed. The technique is based on a grain-boundary integral representation of the polycrystalline micro-mechanics, numerically solved by the boundary element method, coupled with an explicit finite element model of the intergranular hydrogen diffusion. The intergranular interaction between contiguous grains in the aggregate is modelled through extrinsic cohesive-frictional traction-separation laws, whose parameters depend on the concentration of intergranular hydrogen, which diffuses over the interface according to the Fick’s second law, inducing the weakening of the i…
Use of the electrochemical microcell technique and the SVET for monitoring pitting corrosion at MnS inclusions
2004
The purpose of this paper is to report on use of the electrochemical microcell technique and the scanning vibrating electrode technique for monitoring pitting corrosion on the same stainless steel microstructure. First, the electrochemical behaviour of sites containing a single inclusion was investigated in order to the determine both the successive steps occurring during the inclusions activation and some key-parameters such as the onset potential for MnS dissolution and the pitting potential. Then, the local current distribution around a pitting site was monitored at open circuit potential in order to locate anodic and cathodic regions and to obtain informations on the galvanic coupling b…
Measurements of Positrons Lifetimes in Corroded Nickel
1999
It is over twenty years now that the nuclear method of conducting investigations into defects in the volume and on the surface of solids, based on positron annihilation phenomenon, has been developing on a quite intensive scale [1-3]. The present work is an attempt at adopting positron annihilation to investigations of the phenomenon of pitting corrosion in metals. Pitting occurs mainly in environments containing chlorides and affects metals and alloys covered with passivating oxide layers. Research carried out for many years by the use of various methods . has proved that pittings, which could — after some time — take sizes as large as the tenth of the millimeter order, are formed in the p…
Repassivation of the damage generated by cavitation on UNS N08031 in a LiBr solution by means of electrochemical techniques and Confocal Laser Scanni…
2010
Abstract The objective of this work is to study the influence of cavitation on the corrosion behaviour of Alloy 31, a highly-alloyed austenitic stainless steel (UNS N08031), in a LiBr heavy brine solution (992 g/L) at 25 °C. The presence of cavitation shifted the OCP value towards the active direction by 708 mVAg/AgCl, increased anodic current densities and passivation current density, ip, and reduced the pitting potential, Ep. Repassivation behaviour of Alloy 31 has been investigated by using potentiostatic tests at different potentials. The current density transient obtained after interrupting cavitation was used to obtain the repassivation index, n, provided by the slope of the log i(t) …
Investigation of pitting resistance of titanium based on a modified point defect model
2011
Abstract The pitting resistance of titanium was studied under potential control in solutions containing chloride ions. The results evidenced that Cl − concentration had an effect on the metastable pitting intensity, but no significant influence on the uniform corrosion. XPS characterization revealed that some Cl − ions were present in the outer hydroxide layer, but few in the inner oxide layer, indicating that the inner oxide layer was impervious to Cl − ions. A cation–anion-vacancy condensation mechanism was considered for pit initiation based on the point defect model (PDM). The experimental results analyzed by the charge integration technique were in agreement with the derived relations.
Evaluation of metastable pitting on titanium by charge integration of current transients
2010
Abstract The metastable pitting of titanium has been studied under potentiostatic control in solutions containing chloride ions. An approach based on the charge integration of current transients was proposed for a quantitative determination of metastable pitting. A pit density (dmpit) was defined as the number of metastable pits per unit area per unit time (cm−2 h−1) with a typical size, instead of a size distribution. The calculated dmpit of titanium at 0.5 VSCE in 0.6 M NaCl was about 1.0 × 103 cm−2 h−1 with a typical radius of 0.12 μm. An exponential potential dependence of dmpit was obtained through the integration approach.
Influence of an elastic stress on the conductivity of passive films
2001
Abstract The electrochemical impedance was measured over a large range of frequency and under straining condition in sodium chloride solution. The Mott-Schottky analysis, performed at high frequency, appears as very useful method to study the effect of an elastic stress on the capacitance values. The results obtained indicate that the semi-conductive properties of passive films formed on a type 316 L stainless steel (SS) are not markedly modified by an elastic stress when applied after ageing. In contrast, passive films formed in the presence of elastic stress have a higher donor and acceptor concentration than those formed in a stress-free state, suggesting that the passive film conductivi…
Passive Behavior and Passivity Breakdown of AISI 304 in LiBr Solutions through Scanning Electrochemical Microscopy
2014
The passive behavior and passivity breakdown of AISI 304 stainless steel in LiBr solutions has been investigated by means of scanning electrochemical microscopy (SECM). The sample generation - tip collection (SG-TC) mode was used to operate the SECM and the tip potential was biased to detect the electroactive species. The evolution of the current at the ultramicroelectrode tip with the applied potential within the passive range was followed at different LiBr concentrations. Results show that the absolute value of the current at the tip increases with the applied potential. Additionally, SECM was also used to detect stable pits formed on the stainless steel surface in a 0.2 M LiBr solution. …